Our Product Range Stainless Steel Pipes Stainless Steel TubesStainless Steel Tubes ASTM A 312 TP 304L, UNS S30403, 1.4306, X2CrNi19-11 Tubes ASTM A 312 TP 304, UNS S30400, 1.4301, X5CrNi18-10 Tubes ASTM A 312 TP 304H, UNS S30409, 1.4948, X6CrNi18-11 Tubes ASTM A 312 TP 304H, UNS S30415 Tubes ASTM A312 TP 309S, UNS S30908 Tubes ASTM A 312 TP 310H, UNS S31035 Tubes ASTM A 312 TP 310H, UNS S31009 Tubes ASTM A 312 TP 310S, UNS S31008 Tubes ASTM A 312 TP 316, UNS S31600, 1.4401 Tubes ASTM A 312 TP 316L, UNS S31603, 1.4432 Tubes ASTM A 312 TP 316Ti, UNS S31635, X6CrNiMoTi17-12-2 Tubes ASTM 1.4438, X2CrNiMo18-15-4 Tubes ASTM A 312 TP 321, UNS ,S32100, 1.4541, X6CrNiTi18-10 Tubes ASTM A 312 TP 321H, UNS S32109, 1.4878, X12CrNiTi18-9 Tubes Stainless Steel Seamless Pipes Stainless Steel Seamless Tubes Stainless Steel 904 L Pipe Stainless Steel Seamless 446 Grade Pipes Duplex Pipes Carbon Steel Pipes & Tubes Alloy Steel Pipes & Tubes Nickel Alloys Pipes & Tubes Inconel Pipes Hastelloy Pipe Monel Pipes Titanium Pipe Heat Exchange Tubes Stainless Steel Square Tubes Stainless Steel Rectangular Tubes Stainless Steel Seamless & Welded Pipes Steel Pipes API steel pipe Carbon steel pipe Alloy steel pipe spiral steel pipe Stainless Steel Pipe Boiler steel pipe ASTM steel pipe Hot Rolled Steel pipe
|
|
Stainless steel is strong and durable. It has a number of useful properties like that help to make it hard and flexible in use. Stainless steel tubes have good strength and good resistance to corrosion and oxidation at respected temperatures. Stainless steels tubes are used at temperatures up to 1700° F.
|
Rehman is one of the leading masters in Stocking & Importing of Stainless Steel ERW, EFW and Stainless Steel Seamless Pipes and Stainless Steel Seamless tubes. Our supply chain includes its European, Korean , Taiwan & many other Import sources who are highly Renowned and Professional manufacturers acquiring High Level of industry expertise and latest technologies.
Worldwide demand for stainless steel is increasing at a rate of about 5% per annum. Annual consumption is now well over 20 million tones and is rasing in areas such as the construction industry and household appliances. New uses are being continuously found for the attractive appearance, corrosion resistance, low maintenance and strength of stainless steel. Stainless steel is more expensive than standard grades of steel but it has greater resistance to corrosion, needs low maintenance and has no need for painting or other protective coatings. These factors mean stainless steel can be more economically viable once service life and life-cycle costs are considered.
This has made reliable one of the Core & Complete Piping and Tubing solution.
|
|
Send Enquiry
ASTM A 312 TP 304L, UNS S30403, SUS304L, 1.4306, X2CrNi19-11 Tubes
| CHEMICAL COMPOSITION,% (Max) | | C | Mn | P | S | Si | Cr | Ni | N | | 0.04 | 2.00 | 0.05 | 0.030 | 1.00 | 18.0-20.0 | 8.0-13.0 | - | | TENSILE PROPERTIES | | Y.S(Min) | T.S(Min) | ELONGATION(Min)% | GRAIN STRUCTURE
| | Ksi[Mpa] | Ksi[Mpa] | L | T | NOT SPECIFIED | | 25[170] | 70[485] | 35 | 25 | | ANNEALING REQUIREMENTS | | HEAT TREATING TEMP(Min) | | 1900°F[1040°C] | |
Send Enquiry
ASTM A 312 TP 304, UNS S30400, SUS304, 1.4301, X5CrNi18-10 Tubes
| CHEMICAL COMPOSITION,% (Max) | | C | Mn | P | S | Si | Cr | Ni | N | | 0.08 | 2.00 | 0.05 | 0.030 | 1.00 | 18.0-20.0 | 8.0-11.0 | - | | TENSILE PROPERTIES | | Y.S(Min) | T.S(Min) | ELONGATION(Min)% | GRAIN STRUCTURE
| | Ksi[Mpa] | Ksi[Mpa] | L | T | NOT SPECIFIED | | 30[205] | 75[515] | 35 | 25 | | ANNEALING REQUIREMENTS | | HEAT TREATING TEMP(Min) | | 1900°F[1040°C] | |
Send Enquiry ASTM A 312 TP 304H, UNS S30409, 1.4948, X6CrNi18-11 Tubes | CHEMICAL COMPOSITION,% (Max) | | C | Mn | P | S | Si | Cr | Ni | N | | 0.04-0.10 | 2.00 | 0.05 | 0.030 | 1.00 | 18.0-20.0 | 8.0-11.0 | - | | TENSILE PROPERTIES | | Y.S(Min) | T.S(Min) | ELONGATION(Min)% | GRAIN STRUCTURE
| | Ksi[Mpa] | Ksi[Mpa] | L | T | NO.7 OR COARSER | | 30[205] | 75[515] | 35 | 25 | | ANNEALING REQUIREMENTS | | HEAT TREATING TEMP(Min) | | 1900°F[1040°C] | |
Send Enquiry ASTM A 312 TP 304H, UNS S30415 Tubes | CHEMICAL COMPOSITION,% (Max) | | C | Mn | P | S | Si | Cr | Ni | N | | 0.04-0.06 | 0.08 | 0.05 | 0.030 | 1.00-2.00 | 18.0-19.0 | 9.0-10.0 | 0.12-0.18 | | TENSILE PROPERTIES | | Y.S(Min) | T.S(Min) | ELONGATION(Min)% | GRAIN STRUCTURE
| | Ksi[Mpa] | Ksi[Mpa] | L | T | NO.7 OR COARSER | | 42[290] | 87[600] | 35 | 25 | | ANNEALING REQUIREMENTS | | HEAT TREATING TEMP(Min) | | 1900°F[1040°C] | |
Send Enquiry
ASTM A312 TP 309S, UNS S30908 Tubes, SUS309S
| CHEMICAL COMPOSITION,% (Max) | | C | Mn | P | S | Si | Cr | Ni | Mo | N | | 0.08 | 2.00 | 0.05 | 0.030 | 1.00 | 22.0-24.0 | 12.0-15.0 | 0.75 | - |
| TENSILE PROPERTIES | | Y.S(Min) | T.S(Min) | ELONGATION(Min)% | GRAIN STRUCTURE
| | Ksi[Mpa] | Ksi[Mpa] | L | T | NOT SPECIFIED | | 30[205] | 75[515] | 35 | 25 |
| ANNEALING REQUIREMENTS | | HEAT TREATING TEMP(Min) | | 1900°F[1040°C] |
| |
Send Enquiry ASTM A 312 TP 310H, UNS S31035 Tubes | CHEMICAL COMPOSITION,% (Max) | | C | Mn | P | S | Si | Cr | Ni | Cb | N | Cu | B | Other | | 0.04-0.10 | 0.60 | 0.03 | 0.015 | 0.40 | 21.5-23.5 | 23.5-26.5 | 0.30-0.60 | 0.15-0.30 | 2.0-3.5 | 0.002-0.008 | W 2.0-4.0 Co 1.0-2.0 | | TENSILE PROPERTIES | | Y.S(Min) | T.S(Min) | ELONGATION(Min)% | GRAIN STRCUTURE | | Ksi[Mpa] | Ksi[Mpa] | L | T | NO.7 OR COARSER | | 45[310] | 95[655] | 35 | 25 | | ANNEALING REQUIREMENTS | | HEAT TREATING TEMP(Min) | | 1900°F[1040°C] | |
Send Enquiry ASTM A 312 TP 310H, UNS S31009 Tubes | CHEMICAL COMPOSITION,% (Max) | | C | Mn | P | S | Si | Cr | Ni | N | | 0.04-0.10 | 2.00 | 0.05 | 0.030 | 1.00 | 24.0-26.0 | 19.0-22.0 | - |
| TENSILE PROPERTIES | | Y.S(Min) | T.S(Min) | ELONGATION(Min)% | GRAIN STRUCTURE
| | Ksi[Mpa] | Ksi[Mpa] | L | T | NO.6 OR COARSER | | 30[205] | 75[515] | 35 | 25 |
| ANNEALING REQUIREMENTS | | HEAT TREATING TEMP(Min) | | 1900°F[1040°C] |
| |
Send Enquiry
ASTM A 312 TP 310S, UNS S31008, SUS310S Tubes
| CHEMICAL COMPOSITION,% (Max) | | C | Mn | P | S | Si | Cr | Ni | Mo | N | | 0.08 | 2.00 | 0.05 | 0.030 | 1.00 | 24.0-26.0 | 19.0-22.0 | 0.75 | - | | TENSILE PROPERTIES | | Y.S(Min) | T.S(Min) | ELONGATION(Min)% | GRAIN STRUCTURE
| | Ksi[Mpa] | Ksi[Mpa] | L | T | NOT SPECIFIED | | 30[205] | 75[515] | 35 | 25 | | ANNEALING REQUIREMENTS | | HEAT TREATING TEMP(Min) | | 1900°F[1040°C] | |
Send Enquiry
ASTM A 312 TP 316, UNS S31600, SUS316, 1.4401 Tubes
| CHEMICAL COMPOSITION,% (Max) | | C | Mn | P | S | Si | Cr | Ni | Mo | N | | 0.08 | 2.00 | 0.05 | 0.030 | 1.00 | 16.0-18.0 | 11.0-14.0 | 2.00-3.00 | - | | TENSILE PROPERTIES | | Y.S(Min) | T.S(Min) | ELONGATION(Min)% | GRAIN STRUCTURE
| | Ksi[Mpa] | Ksi[Mpa] | L | T | NOT SPECIFIED | | 30[205] | 75[515] | 35 | 25 | | ANNEALING REQUIREMENTS | | HEAT TREATING TEMP(Min) | | 1900°F[1040°C] | |
Send Enquiry
ASTM A 312 TP 316L, UNS S31603, SUS316L, 1.4432 Tubes
| CHEMICAL COMPOSITION,% (Max) | | C | Mn | P | S | Si | Cr | Ni | Mo | N | | 0.04 | 2.00 | 0.05 | 0.030 | 1.00 | 16.0-18.0 | 10.0-14.0 | 2.00-3.00 | - | | TENSILE PROPERTIES | | Y.S(Min) | T.S(Min) | ELONGATION(Min)% | GRAIN STRUCTURE
| | Ksi[Mpa] | Ksi[Mpa] | L | T | NOT SPECIFIED | | 25[170] | 70[485] | 35 | 25 | | ANNEALING REQUIREMENTS | | HEAT TREATING TEMP(Min) | | 1900°F[1040°C] | |
Send Enquiry
ASTM A 312 TP 316Ti, UNS S31635, SUS316Ti, X6CrNiMoTi17-12-2 Tubes
| CHEMICAL COMPOSITION,% (Max) | | C | Mn | P | S | Si | Cr | Ni | Mo | TI | N | | 0.08 | 2.00 | 0.05 | 0.030 | 0.75 | 16.0-18.0 | 10.0-14.0 | 2.00-3.00 | 5×(C+N)-0.70 | 0.10 | | TENSILE PROPERTIES | | Y.S(Min) | T.S(Min) | ELONGATION(Min)% | GRAIN STRUCTURE
| | Ksi[Mpa] | Ksi[Mpa] | L | T | NOT SPECIFIED | | 30[205] | 75[515] | 35 | 25 | | ANNEALING REQUIREMENTS | | HEAT TREATING TEMP(Min) | | 1900°F[1040°C] | |
Send Enquiry ASTM 1.4438, X2CrNiMo18-15-4 Tubes
| CHEMICAL COMPOSITION,% (Max) | | C | Mn | P | S | Si | Cr | Ni | Mo | N | | 0.04 | 2.00 | 0.05 | 0.030 | 1.00 | 18.0-20.0 | 11.0-15.0 | 3.00-4.00 | - |
| TENSILE PROPERTIES | | Y.S(Min) | T.S(Min) | ELONGATION(Min)% | GRAIN STRUCTURE
| | Ksi[Mpa] | Ksi[Mpa] | L | T | NOT SPECIFIED | | 30[205] | 75[515] | 35 | 25 |
| ANNEALING REQUIREMENTS | | HEAT TREATING TEMP(Min) | | 1900°F[1040°C] |
| |
Send Enquiry
ASTM A 312 TP 321, UNS ,S32100, SUS321, 1.4541, X6CrNiTi18-10 Tubes
| CHEMICAL COMPOSITION,% (Max) | | C | Mn | P | S | Si | Cr | Ni | Ti | N | | 0.08 | 2.00 | 0.05 | 0.030 | 1.00 | 17.0-19.0 | 9.0-12.0 | < 5×C & >0.70 | 0.1 | | TENSILE PROPERTIES | | | Y.S(Min) | T.S(Min) | ELONGATION(Min)% | GRAIN STRCUTURE | | | Ksi[Mpa] | Ksi[Mpa] | L | T | NOT SPECIFIED | | WELDED | 30[205] | 75[515] | 35 | 25 | | SEAMLESS | | | | | | = ? in. | 30[205] | 75[515] | | | | >? in. | 25[170] | 70[485] | | | | ANNEALING REQUIREMENTS | | HEAT TREATING TEMP(Min) | | 1900°F[1040°C] | |
Send Enquiry ASTM A 312 TP 321H, UNS S32109, 1.4878, X12CrNiTi18-9 Tubes | CHEMICAL COMPOSITION,% (Max) | | C | Mn | P | S | Si | Cr | Ni | Ti | N | | 0.04-0.10 | 2.00 | 0.05 | 0.030 | 1.00 | 17.0-19.0 | 9.0-12.0 | < 4×C & > 0.60 | - | | TENSILE PROPERTIES | | | Y.S(Min) | T.S(Min) | ELONGATION(Min)% | GRAIN STRCUTURE | | | Ksi[Mpa] | Ksi[Mpa] | L | T | NO.7 OR COARSER | | WELDED | 30[205] | 75[515] | 35 | 25 | | SEAMLESS | | | | | | = 3/16 in. | 30[205] | 75[515] | | | | > 3/16 in. | 25[170] | 70[480] | | | | ANNEALING REQUIREMENTS | | HEAT TREATING TEMP(Min) | | 1900°F[1040°C] | |
Send Enquiry
|
| 
| 
| 